CURTAIN WALLING

Curtain wall is a term used to describe a building façade which does not carry any dead load from the building other than its own dead load. These loads are transferred to the main building structure through connections at floors or columns of the building. A curtain wall is designed to resist air and water infiltration, wind forces acting on the building, seismic forces, and its own dead load forces.
Curtain walls are typically designed with extruded aluminium members, although the first curtain walls were made of steel. The aluminium frame is typically infilled with glass, which provides an architecturally pleasing building, as well as benefits such as daylighting. However, parameters related to solar gain control, such as thermal comfort and visual comfort are more difficult to control when using highly-glazed curtain walls. Other common infills include: stone veneer, metal panels, louvers, and operable windows or vents.
Curtain walls differ from storefront systems in that they are designed to span multiple floors, and take into consideration design requirements such as: thermal expansion and contraction; building sway and movement; water diversion; and thermal efficiency for cost-effective heating, cooling, and lighting in the building.

Curtain wall is used to describe the set of walls that surround and protect the interior (bailey) of a medieval castle. These walls are often connected by a series of towers or mural towers to add strength and provide for better defense of the ground outside the castle, and are connected like a curtain draped between these posts. Additional provisions and buildings were often enclosed by such a construction, designed to help a garrison last longer during a siege by enemy forces. Examples of curtain walls as part of castles are at Muchalls Castle, Scotland and Dunstanburgh Castle, England, the latter of which is in a ruined state.

Prior to the middle of the nineteenth century, buildings were constructed with the exterior walls of the building (bearing walls, typically masonry) supporting the load of the entire structure. The development and widespread use of structural steel and later reinforced concrete allowed relatively small columns to support large loads and the exterior walls of buildings were no longer required for structural support. The exterior walls could be non-bearing, and thus much lighter and more open than the masonry bearing walls of the past. This gave way to increased use of glass as an exterior façade, and the modern day curtain wall was born.
The first curtain walls were made with steel mullions, and the plate glass was attached to the mullions with asbestos or fiberglass modified glazing compound. Eventually silicone sealants or glazing tape were substituted. Some designs included an outer cap to hold the glass in place and to protect the integrity of the seals. The first curtain wall installed in New York City was this type of construction. Earlier modernist examples are the Bauhaus in Dessau and the Hallidie Building in San Francisco. The 1970’s began the widespread use of aluminum extrusions for mullions. Aluminum offers the unique advantage of being able to be easily extruded into nearly any shape required for design and aesthetic purposes. Today, the design complexity and shapes available are nearly limitless. Custom shapes can be designed and manufactured with relative ease.
Similarly, sealing methods and types have evolved over the years, and as a result, today’s curtain walls are high performance systems which require little maintenance.
Stick systems
The vast majority of curtain walls are installed long pieces (referred to as sticks) between floors vertically and between vertical members horizontally. Framing members may be fabricated in a shop environment, but all installation and glazing is typically performed at the jobsite.
Unitized systems
Unitized curtain walls entail factory fabrication and assembly of panels and may include factory glazing. These completed units are hung on the building structure to form the building enclosure. Unitized curtain wall has the advantages of: speed; lower field installation costs; and quality control within an interior climate controlled environment. The economic benefits are typically realized on large projects or in areas of high field labor rates.
Rainscreen principle
A common feature in curtain wall technology, the rainscreen principle theorizes that equilibrium of air pressure between the outside and inside of the "rainscreen" prevents water penetration into the building itself. For example the glass is captured between an inner and an outer gasket in a space called the glazing rebate. The glazing rebate is ventilated to the exterior so that the pressure on the inner and outer sides of the exterior gasket is the same. When the pressure is equal across this gasket water cannot be drawn through joints or defects in the gasket.

Design
Curtain wall systems must be designed to handle all loads imposed on it as well as keep air and water from penetrating the building envelope.

Loads
The loads imposed on the curtain wall are transferred to the building structure through the anchors which attach the mullions to the building. The building structure needs to be designed and account for these loads.
Dead load
Dead load is defined as the weight of structural elements and the permanent features on the structure. In the case of curtain walls, this load is made up of the weight of the mullions, anchors, and other structural components of the curtain wall, as well as the weight of the infill material. Additional dead loads imposed on the curtain wall, such as sunshades, must be accounted for in the design of the curtain wall components and anchors.
Wind load
Wind load acting on the building is the result of wind blowing on the building. This wind pressure must be resisted by the curtain wall system since it envelops and protects the building. Wind loads vary greatly throughout the world, with the largest wind loads being near the coast in hurricane-prone regions. Building codes are used to determine the required design wind loads for a specific project location. Often, a wind tunnel study is performed on large or unusually shaped buildings. A scale model of the building and the surrounding vicinity is built and placed in a wind tunnel to determine the wind pressures acting on the structure in question. These studies take into account vortex shedding around corners and the effects of surrounding buildings.
Seismic load
Seismic loads need to be addressed in the design of curtain wall components and anchors. In most situations, the curtain wall is able to naturally withstand seismic and wind induced building sway because of the space provided between the glazing infill and the mullion. In tests, standard curtain wall systems are able to withstand three inches (75 mm) of relative floor movement without glass breakage or water leakage. Anchor design needs to be reviewed, however, since a large floor-to-floor displacement can place high forces on anchors.
Snow load
Snow loads and live loads are not typically an issue in curtain walls, since curtain walls are designed to be vertical or slightly inclined. If the slope of a wall exceeds 20 degrees or so, these loads may need to be considered.
Thermal load
Thermal loads are induced in a curtain wall system because aluminum has a relatively high coefficient of thermal expansion. This means that over the span of a couple of floors, the curtain wall will expand and contract some distance, relative to its length and the temperature differential. This expansion and contraction is accounted for by cutting horizontal mullions slightly short and allowing a space between the horizontal and vertical mullions. In unitized curtain wall, a gap is left between units, which is sealed from air and water penetration by wiper gaskets. Vertically, anchors carrying wind load only (not dead load) are slotted to account for movement. Incidentally, this slot also accounts for live load deflection and creep in the floor slabs of the building structure.
Blast load
Accidental explosions and terrorist threats have brought on increased concern for the fragility of a curtain wall system in relation to blast loads. The bombing of the Alfred P. Murrah Federal Building in Oklahoma City, Oklahoma, has spawned much of the current research and mandates in regards to building response to blast loads. Currently, all new federal buildings in the U.S., and all U.S. embassies built on foreign soil, must have some provision for resistance to bomb blasts.
Since the curtain wall is at the exterior of the building, it becomes the first line of defense in a bomb attack. As such, blast resistant curtain walls must be designed to withstand such forces without compromising the interior of the building to protect its occupants. Since blast loads are very high loads with short durations, the curtain wall response should be analyzed in a dynamic load analysis, with full-scale mock-up testing performed prior to design completion and installation.
Blast resistant glazing consists of laminated glass, which is meant to break but not separate from the mullions. Similar technology is used in hurricane-prone areas for the protection from wind-borne debris.

Infiltration
Air infiltration is the air which passes through the curtain wall from the exterior to the interior of the building. The air is infiltrated through the gaskets, through imperfect joinery between the horizontal and vertical mullions, through weep holes, and through imperfect sealing. The American Architectural Manufacturers Association (AAMA) is the governing body in the U.S. which sets the acceptable levels of air infiltration through a curtain wall. This limit is expressed (in America) in cubic feet per minute per square foot of wall area at a given test pressure. (Currently, most standards cite less than 0.6 CFM/sq ft as acceptable).
Water penetration is defined as any water passing from the exterior of the building through to the interior of the curtain wall system. Sometimes, depending on the building specifications, a small amount of controlled water on the interior is deemed acceptable. To test the ability of a curtain wall to withstand water penetration, a water rack is placed in front a mock-up of the wall with a positive air pressure applied to the wall. This represents a wind driven heavy rain on the wall. Field tests are also performed on installed curtain walls, in which a water hose is sprayed on the wall for a specified time.

Deflection
One of the disadvantages of using aluminum for mullions is that its modulus of elasticity is about one-third that of steel. This translates to three times more deflection in an aluminum mullion compared to the same steel section under a given a load. Building specifications set deflection limits for perpendicular (wind-induced) and in-plane (dead load-induced) deflections. It is important to note that these deflection limits are not imposed due to strength capacities of the mullions. Rather, they are designed to limit deflection of the glass (which may break under excessive deflection), and to ensure that the glass does not come out of its pocket in the mullion. Deflection limits are also necessary to control movement at the interior of the curtain wall. Building construction may be such that there is a wall located near the mullion, and excessive deflection can cause the mullion to contact the wall and cause damage. Also, if deflection of a wall is quite noticeable, public perception may raise undue concern that the wall is not strong enough.
Deflection limits are typically expressed as the distance between anchor points divided by a constant number. A deflection limit of L/175 is common in curtain wall specifications, based on experience with deflection limits that are unlikely to cause damage to the glass help by the mullion. Say a given curtain wall is anchored at 12 foot (144 in) floor heights. The allowable deflection would then be 144/175 = 0.823 inches, which means the wall is allowed to deflect inward or outward a maximum of 0.823 inches at the maximum wind pressure.
Deflection in mullions is controlled by different shapes and depths of curtain wall members. The depth of a given curtain wall system is usually controlled by the area moment of inertia required to keep deflection limits under the specification. Another way to limit deflections in a given section is to add steel reinforcement to the inside tube of the mullion. Since steel deflects at 1/3 the rate of aluminum, the steel will resist much of the load at a lower cost or smaller Stress

Contrary to popular belief, stress is not related to deflection; it is a separate criterion in curtain wall design and analysis. For example, the advantage of some curtain wall designs is the ability to span more than one floor (commonly known as twin-span or multi-span, as opposed to single or simple span). Multiple floor spans significantly reduce the required area moment of inertia for a mullion. The stresses in the mullion, however, are significantly increased in a multiple span, giving way for a higher required section modulus (S, expressed in cubic inches) in the mullion.
As mentioned above, the deflection of aluminum is three times greater than an equivalent steel shape under the same load. However, the allowable stress in that same aluminum member may be roughly equivalent to or higher than its steel counterpart. This means that aluminum mullions can be as strong as or stronger than st Thermal criteria

Relative to other building components, aluminum has a high heat transfer coefficient, meaning that aluminum is a very good conductor of heat. This translates into high heat loss through aluminum curtain wall mullions. There are several ways to compensate for this heat loss, the most common way being the addition of thermal breaks. Thermal breaks are barriers between exterior metal and interior metal, usually made of polyvinyl chloride (PVC). These breaks provide a significant decrease in the thermal conductivity of the curtain wall. However, since the thermal break interrupts the aluminum mullion, the overall moment of inertia of the mullion is reduced and must be accounted for in the structural analysis of the system.
Thermal conductivity of the curtain wall system is important because of heat loss through the wall, which affects the heating and cooling costs of the building. On a poorly performing curtain wall, condensation may form on the interior of the mullions. This could cause damage to adjacent interior trim and walls.
Rigid insulation is provided in spandrel areas to provide a higher R-value at these locations.

Infills
Infill refers to the large panels that are inserted into the curtain wall between mullions. Infills are typically glass but may be made up of nearly any exterior building element.
Regardless of the material, infills are typically referred to as glazing, and the installer of the infill is referred to as a glazier

By far the most common glazing type, glass can be of an almost infinite combination of color, thickness, and opacity. For commercial construction, the two most common thicknesses are 1/4 inch (6 mm) monolithic and 1 inch (25 mm) insulating glass. Presently, 1/4 inch glass is typically used only in spandrel areas, while insulating glass is used for the rest of the building (sometimes spandrel glass is specified as insulating glass as well). The 1 inch insulation glass is typically made up of two 1/4-inch lites of glass with a 1/2 inch (12 mm) airspace. The air inside is usually atmospheric air, but some inert gases, such as argon, may be used to offer better thermal transmittance values. In residential construction, thicknesses commonly used are 1/8 inch (3 mm) monolithic and 5/8 inch (16 mm) insulating glass. Larger thicknesses are typically employed for buildings or areas with higher thermal, relative humidity, or sound transmission requirements, such as laboratory areas or recording studios.
Glass may be used which is transparent, translucent, or opaque, or in varying degrees thereof. Transparent glass usually refers to vision glass in a curtain wall. Spandrel or vision glass may also contain translucent glass, which could be for security or aesthetic purposes. Opaque glass is used in areas to hide a column or spandrel beam or shear wall behind the curtain wall. Another method of hiding spandrel areas is through shadow box construction (providing a dark enclosed space behind the transparent or translucent glass). Shadow box construction creates a perception of depth behind the glass that is sometimes desired.

Stone veneer
Thin blocks (3 to 4 inches (75-100 mm)) of stone can be inset within a curtain wall system to provide architectural flavor. The type of stone used is limited only by the strength of the stone and the ability to manufacture it in the proper shape and size. Common stone types used are: Arriscraft(calcium silicate);granite; marble; travertine; and limestone. The stone may come in several different finishes, which adds many more options for architects and building owners.

Panels
Metal panels can take various forms including aluminum plate; thin composite panels consisting of two thin aluminum sheets sandwiching a thin plastic interlayer; and panels consisting of metal sheets bonded to rigid insulation, with or without an inner metal sheet to create a sandwich panel. Other opaque panel materials include FRP (fiber-reinforced plastic) and stainless steel.

Louvers
A louver is provided in an area where mechanical equipment located inside the building requires ventilation or fresh air to operate. They can also serve as a means of allowing outside air to filter into the building to take advantage of favorable climatic conditions and minimize the usage of energy-consuming HVAC systems. Curtain wall systems can be adapted to accept most types of louver systems to maintain the same architectural sightlines and style while providing the necessary functionality.

Windows and vents
Most curtain wall glazing is fixed, meaning there is no access to the exterior of the building except through doors. However, windows or vents can be glazed into the curtain wall system as well, to provide required ventilation or operable windows. Nearly any window type can be made to fit into a curtain wall system.

Maintenance and repair
Curtain walls and perimeter sealants require maintenance to maximize service life. Perimeter sealants, properly designed and installed, have a typical service life of 10 to 15 years. Removal and replacement of perimeter sealants require meticulous surface preparation and proper detailing.
Aluminum frames are generally painted or anodized. Factory applied fluoropolymer thermoset coatings have good resistance to environmental degradation and require only periodic cleaning. Recoating with an air-dry fluoropolymer coating is possible but requires special surface preparation and is not as durable as the baked-on original coating.
Anodized aluminum frames cannot be "re-anodized" in place, but can be cleaned and protected by proprietary clear coatings to improve appearance and durability.
Exposed glazing seals and gaskets require inspection and maintenance to minimize water penetration, and to limit exposure of frame seals and insulating glass seals to wetting.

TYPE OF BRICK

Engineering bricks

London bricks or Flettons

Extruded or wirecut bricks

stock brick

Stock bricks

Traditional type of brick with a slightly irregular shape.
Made by using a mechanised moulding process known as soft mud moulding.
A wide range of colours are available.
In price, as well as style, stock bricks fall between the wirecuts and the handmades.
Currently one of the most popular with self-builders.
Extruded or wirecut bricks
Suitable for almost every type of application.
Available in a wide range of colours and textures.
Made by extrusion of a continuous column of clay which, as the name implies, is cut by the wire.
Surface textures can be applied by additions of sand or texturing the face e.g. rusticated or dragfaced.
Highly automated production process makes wirecuts relatively inexpensive compared to some other types of brick.

London bricks or Flettons

London bricks are only manufactured by Hanson.
Made from deposits of Oxford clay, require little fuel to fire them and so are one of the most economically priced bricks.
Available in a wide range of colours and textures.
Popular for matching existing brickwork.
Extruded tumbled bricks
Distressed irregular shaped bricks.
Made by extruding and then rolling in a drum, distressing the edges and giving an irregular feel with a rounder softer look to the brick.
Offers a value for money natural look.

Engineering bricks

Used for their performance characteristics rather than their appearance
Most suited for ground works, manholes and sewers, retaining walls and other situations where strength and resistance to frost attack and water are the most important factor.

Special shaped bricks
Enable flexible design and the means to execute any imaginative design detail or decorative element.
Adds a high quality finish to brickwork. Can provide extra durability and protection to vulnerable areas and can save time on-site by overcoming extensive hand cuttin. Over 70 special shapes are available from Hanson consisting of both standard and purpose made shapes.

SLUMP TEST

Slump test

Description:

The slump test is a means of assessing the consistency of fresh concrete. It is used, indirectly, as a means of checking that the correct amount of water has been added to the mix. The test is carried out in accordance with BS EN 12350-2, Testing fresh concrete. Slump test. This replaces BS 1881: Part 102.
The steel slump cone is placed on a solid, impermeable, level base and filled with the fresh concrete in three equal layers. Each layer is rodded 25 times to ensure compaction. The third layer is finished off level with the top of the cone. The cone is carefully lifted up, leaving a heap of concrete that settles or ‘slumps’ slightly. The upturned slump cone is placed on the base to act as a reference, and the difference in level between its top and the top of the concrete is measured and recorded to the nearest 5 mm to give the slump of the concrete.
When the cone is removed, the slump may take one of three forms. In a true slump the concrete simply subsides, keeping more or less to shape. In a shear slump the top portion of the concrete shears off and slips sideways. In a collapse slump the concrete collapses completely. Only a true slump is of any use in the test. If a shear or collapse slump is achieved, a fresh sample should be taken and the test repeated. A collapse slump will generally mean that the mix is too wet or that it is a high workability mix, for which the flow test (see separate entry) is more appropriate.

Acknowledgement:
The Concrete Society
Book links:Click image/title for more information

MY BROCHURE

This is my original brochure...
Here i just explain about my company ' mahligai construction sdn.bhd'my company worked as s business in material and equipment in construction...
Furthermore, i explain about my vision and mission my company and others..
I also explain about our company activities on that years...
In addition, i explain about our promotion to all businessman and our customers to joint our company...
In that case, it can be easier to all customers and businessman to connected with us and it is also easy for us to communicate to worked the business...
That all i can explain a bout my brochure....

image of concrete

CONCRETE

Concrete

A concrete slab ponded while curing

Concrete columns curing while wrapped in plastic
Concrete is a construction material that consists of cement (commonly Portland cement) as well as other cementitious materials such as fly ash and slag cement, aggregate (generally a coarse aggregate such as gravel limestone or granite, plus a fine aggregate such as sand and water) and chemical admixtures.
Concrete solidifies and hardens after mixing and placement due to a chemical process known as hydration.The water reacts with the cement, which bonds the other components together, eventually creating a stone-like material. It is used to make pavements, architectural structures, foundations, motorways/roads, overpasses, parking structures, brick/block walls and footings for gates, fences and poles.
More concrete is used than any other man-made material on the planet. As of 2006 about seven billion cubic meters of concrete are made each year – more than one cubic meter for every person on Earth. Concrete powers a US$35 billion industry which employs more than two million workers in the United States alone. More than 55,000 miles of freeways and highways in America are made of this material. The People's Republic of China currently consumes 40% of the world's cement [concrete] production.

History

The word concrete comes from the Latin word "concretus" which means "to harden".
In Serbia, remains of a hut dating from 5600 BC have been found, with a floor made of red lime, sand, and gravel. The pyramids of Shaanxi in China, built thousands of years ago, contain a mixture of lime and volcanic ash or clay.
The Assyrians and Babylonians used clay as cement in their concrete. The Egyptians used lime and gypsum cement.
During the Roman Empire, Roman concrete made from quicklime, pozzolanic ash/pozzolana and an aggregate made from pumice was very similar to modern Portland cement concrete.
The secret of concrete was lost for 13 centuries until in 1756, the British engineer John Smeaton pioneered the use of hydraulic lime in concrete, using pebbles and powdered brick as aggregate. Portland cement was first used in concrete in the early 1840s.
In modern times the use of recycled materials as concrete ingredients is gaining popularity because of increasingly stringent environmental legislation. The most conspicuous of these is fly ash, a byproduct of coal fired power plants. This has a significant impact by reducing the amount of quarrying and landfill space required, and, as it acts as a cement replacement, reduces the amount of cement required to produce a solid concrete. As cement production creates massive quantities of carbon dioxide, cement replacement technology such as this will play a huge role in future attempts to cut CO2.
Concrete additives have been used since Roman and Egyptian times, when it was discovered that adding volcanic ash to the mix allowed it to set under water. Similarly, the Romans knew that adding horse hair made concrete less liable to crack while it hardened, and adding blood made it more frost resistant.
In modern times, researchers have experimented with the addition of other materials to create concrete with improved properties, such as higher strength or electrical conductivity.

Composition

A highway paved with concrete.

1930s vibrated concrete, manufactured in Croydon and installed by the LMS railway after an art deco refurbishment in Meols.
There are many types of concrete available by varying the proportions of the main ingredients below.
The mix design depends on the type of structure being built, how the concrete will be mixed and delivered, and how it will be placed to form this structure.

Cement

Portland cement is the most common type of cement in general usage. It is a basic ingredient of concrete, mortar and plaster. English engineer Joseph Aspdin patented Portland cement in 1824; it was named because of its similarity in colour to Portland limestone, quarried from the English Isle of Portland and used extensively in London architecture. It consists of a mixture of oxides of calcium, silicon and aluminium. Portland cement and similar materials are made by heating limestone (a source of calcium) with clay, and grinding this product (called clinker) with a source of sulfate (most commonly gypsum).
High temperature applications, such as masonry ovens and the like, generally require the use of a refractory cement; concretes based on Portland cement can be damaged or destroyed by elevated temperatures, but refractory concretes are better able to withstand such conditions.

Water

Combined with a cementitious material, this forms a cement paste. The cement paste glues the aggregate together, fills voids between it, and allows it to flow more easily.
Less water in the cement paste will yield a stronger more durable concrete, more water will give an easier flowing concrete with a higher slump.[4]
Impure water used to make concrete can cause problems, either when setting, or later on.

Aggregates

Fine and coarse aggregates make up the bulk of a concrete mixture. Sand, natural gravel and crushed stone are mainly used for this purpose. Recycled aggregates (from construction, demolition and excavation waste) are increasingly used as partial replacements of natural aggregates, while a number of manufactured aggregates, including air-cooled blast furnace slag and bottom ash are also permitted.
Decorative stones such as quartzite, small river stones or crushed glass are sometimes added to the surface of concrete for a decorative "exposed aggregate" finish, popular among landscape designers.

Reinforcement

Concrete is strong in compression, as the aggregate efficiently carries the compression load. However, it is weak in tension as the cement holding the aggregate in place can snap, allowing the structure to fail. Reinforced concrete solves these problems by adding metal reinforcing bars, glassfiber, or plastic fiber to carry tensile loads.

Chemical admixtures

Chemical admixtures are materials in the form of powder or fluids that are added to the concrete to give it certain characteristics not obtainable with plain concrete mixes. In normal use, admixture dosages are less than 5% by mass of cement, and are added to the concrete at the time of batching/mixing.[5] The most common types of admixtures are:
Accelerators speed up the hydration (hardening) of the concrete.
Retarders slow the hydration of concrete, and are used in large or difficult pours where partial setting before the pour is complete is undesirable.
Air-entrainers add and distribute tiny air bubbles in the concrete, which will reduce damage during freeze-thaw cycles thereby increasing the concrete's durability. However, entrained air is a trade-off with strength, as each 1% of air may result in 5% decrease in compressive strength.
Plasticizers (water-reducing admixtures) increase the workability of plastic or "fresh" concrete, allowing it be placed more easily, with less consolidating effort.
Superplasticizers (high-range water-reducing admixtures) are a class of plasticizers which have fewer deleterious effects when used to significantly increase workability. Alternatively, plasticizers can be used to reduce the water content of a concrete (and have been called water reducers due to this application) while maintaining workability. This improves its strength and durability characteristics.
Pigments can be used to change the color of concrete, for aesthetics.
Corrosion inhibitors are used to minimize the corrosion of steel and steel bars in concrete.
Bonding agents are used to create a bond between old and new concrete.
Pumping aids improve pumpability, thicken the paste, and reduce dewatering – the tendency for the water to separate out of the paste.

Mineral admixtures and blended cements

There are inorganic materials that also have pozzolanic or latent hydraulic properties. These very fine-grained materials are added to the concrete mix to improve the properties of concrete (mineral admixtures),[5] or as a replacement for Portland cement (blended cements).
Fly ash: A by product of coal fired electric generating plants, it is used to partially replace Portland cement (by up to 60% by mass). The properties of fly ash depend on the type of coal burnt. In general, silicious fly ash is pozzolanic, while calcareous fly ash has latent hydraulic properties.
Ground granulated blast furnace slag (GGBFS or GGBS): A by product of steel production, is used to partially replace Portland cement (by up to 80% by mass). It has latent hydraulic properties.
Silica fume: A byproduct of the production of silicon and ferrosilicon alloys. Silica fume is similar to fly ash, but has a particle size 100 times smaller. This results in a higher surface to volume ratio and a much faster pozzolanic reaction. Silica fume is used to increase strength and durability of concrete, but generally requires the use of superplasticizers for workability.
High Reactivity Metakaolin (HRM): Metakaolin produces concrete with strength and durability similar to concrete made with silica fume. While silica fume is usually dark gray or black in color, high reactivity metakaolin is usually bright white in color, making it the preferred choice for architectural concrete where appearance is important.

Mixing concrete

Thorough mixing is essential for the production of uniform, high quality concrete. Therefore, equipment and methods should be capable of effectively mixing concrete materials containing the largest specified aggregate to produce uniform mixtures of the lowest slump practical for the work. Separate paste mixing has shown that the mixing of cement and water into a paste before combining these materials with aggregates can increase the compressive strength of the resulting concrete.[10] The paste is generally mixed in a high-speed, shear-type mixer at a w/cm of 0.30 to 0.45 by mass. The premixed paste is then blended with aggregates and any remaining batch water, and final mixing is completed in conventional concrete mixing equipment.

High-Energy Mixed Concrete (HEM concrete) is produced by means of high-speed mixing of cement, water and sand with net specific energy consumption at least 5 kilojoules per kilogram of the mix. It is then added to a plasticizer admixture and mixed after that with aggregates in conventional mixer. This paste can be used itself or foamed (expanded) for lightweight concrete.[12] Sand effectively dissipates energy in this mixing process. HEM concrete fast hardens in ordinary and low temperature conditions, and possesses increased volume of gel, drastically reducing capillarity in solid and porous materials. It is recommended for precast concrete in order to reduce quantity of cement, as well as concrete roof and siding tiles, paving stones and lightweight concrete block production.

Characteristics

During hydration and hardening, concrete needs to develop certain physical and chemical properties. Among other qualities, mechanical strength, low moisture permeability, and chemical and volumetric stability are necessary.

Workability

Workability is the ability of a fresh (plastic) concrete mix to fill the form/mold properly with the desired work (vibration) and without reducing the concrete's quality. Workability depends on water content, aggregate (shape and size distribution), cementitious content and age (level of hydration), and can be modified by adding chemical admixtures. Raising the water content or adding chemical admixtures will increase concrete workability. Excessive water will lead to increased bleeding (surface water) and/or segregation of aggregates (when the cement and aggregates start to separate), with the resulting concrete having reduced quality. The use of an aggregate with an undesirable gradation can result in a very harsh mix design with a very low slump, which cannot be readily made more workable by addition of reasonable amounts of water.
Workability can be measured by the "slump test," a simplistic measure of the plasticity of a fresh batch of concrete following the ASTM C 143 or EN 12350-2 test standards. Slump is normally measured by filling an "Abrams cone" with a sample from a fresh batch of concrete. The cone is placed with the wide end down onto a level, non-absorptive surface. It is then filled in three layers of equal volume, with each layer being tamped with a steel rod in order to consolidate the layer. When the cone is carefully lifted off, the enclosed material will slump a certain amount due to gravity. A relatively dry sample will slump very little, having a slump value of one or two inches (25 or 50 mm). A relatively wet concrete sample may slump as much as six or seven inches (150 to 175 mm).
Slump can be increased by adding chemical admixtures such as mid-range or high-range water reducing agents (super-plasticizers) without changing the water/cement ratio. It is bad practice to add excessive water upon delivery to the jobsite, however in a properly designed mixture it is important to reasonably achieve the specified slump prior to placement as design factors such as air content, internal water for hydration/strength gain, etc. are dependent on placement at design slump values.
High-flow concrete, like self-consolidating concrete, is tested by other flow-measuring methods. One of these methods includes placing the cone on the narrow end and observing how the mix flows through the cone while it is gradually lifted.

Curing

In all but the least critical applications, care needs to be taken to properly cure concrete, and achieve best strength and hardness. This happens after the concrete has been placed.
Cement requires a moist, controlled environment to cure – hydrate – fully.
The cement paste hardens over time, initially setting and becoming rigid though very weak, and gaining in strength in the days and weeks following.
It does not set by drying out, but by the cementitious material chemically reacting with the water – hydrating. The pictures above show two of many ways to achieve this, ponding – submerging setting concrete in water, and wrapping in plastic to contain the water in the mix.
Properly curing concrete leads to increased strength and lower permeability, and avoids cracking where the surface dries out prematurely.
Care must also be taken to avoid freezing, or overheating due to the exothermic setting of cement.
Improper curing can cause scaling, reduced strength and abrasion resistance and cracking.

Strength

Concrete has relatively high compressive strength, but significantly lower tensile strength (about 10% of the compressive strength). As a result, without compensating, concrete would almost always fail from tensile stresses – even when loaded in compression. The practical implication of this is that concrete elements subjected to tensile stresses must be reinforced with materials that are strong in tension. Concrete is most often constructed with the addition of steel or fiber reinforcement. The reinforcement can be by bars (rebar), mesh, or fibres, which provide the required tensile strength to concrete producing reinforced concrete. Concrete can also be prestressed (reducing tensile stress) using internal steel cables (tendons), allowing for beams or slabs with a longer span than is practical with reinforced concrete alone. Inspection of concrete structures can be non-destructive if carried out with equipment such as a Schmidt hammer, which is used to estimate concrete strength.
The ultimate strength of concrete is influenced by the water-cement ratio (w/c), the design constituents, and the mixing, placement and curing methods employed. All things being equal, concrete with a lower water-cement (cementitious) ratio makes a stronger concrete than that with a higher ratio. The total quantity of cementitious materials (Portland cement, slag cement, pozzolans) can affect strength, water demand, shrinkage, abrasion resistance and density. All concrete will crack independent of whether or not it has sufficient compressive strength. In fact, high portland cement content mixtures actually crack earlier due to increased hydration rate. As concrete transforms from its plastic state, hydrating to a solid, the material undergoes shrinkage. Plastic shrinkage cracks can occur soon after placement but if the evaporation rate is high they often can actually occur during finishing operations, for example in hot weather or a breezy day. In very high strength concrete mixtures (greater than 10,000 psi) the crushing strength of the aggregate can be a limiting factor to the ultimate compressive strength. In lean concretes (with a high water-cement ratio) the crushing strength of the aggregates is not so significant.
Experimentation with various mix designs begins by specifying desired "workability" as defined by a given slump, "durability" requirements taking into consideration the weather exposure conditions (freeze-thaw) to which the concrete will be exposed in service, and the required "28 day compressive strength" as determined by properly molded standard-cured cylinder samples. The characteristics of the cementitious content, coarse and fine aggregates, and chemical admixtures determine the water demand of the mix in order to achieve the desired workability. The 28 day compressive strength is obtained by determination of the correct amount of cementitious (and often chemical admixtures) to achieve the target water-cementitious ratio.
The internal forces in common shapes of structure, such as arches, vaults, columns and walls are predominantly compressive forces, with floors and pavements subjected to tensile forces. Compressive strength is widely used for specification requirement and quality control of concrete. The engineer knows his target tensile (flexural) requirements and will express these in terms of compressive strength.
Wired.com reported on April 13, 2007 that a team from the University of Tehran, competing in a contest sponsored by the American Concrete Institute, demonstrated several blocks of concretes with abnormally high compressive strengths between 50,000 and 60,000 PSI at 28 days.[13] The blocks appeared to use an aggregate of steel fibres and quartz – a mineral with a compressive strength of 160,000 PSI, much higher than typical high-strength aggregates such as granite (15,000-20,000 PSI).

Elasticity

The modulus of elasticity of concrete is a function of the modulus of elasticity of the aggregates and the cement matrix and their relative proportions. The modulus of elasticity of concrete is relatively linear at low stress levels but becomes increasingly non-linear as matrix cracking develops. The elastic modulus of the hardened paste may be in the order of 10-30 GPa and aggregates about 45 to 85 GPa. The concrete composite is then in the range of 30 to 50 GPa.

Expansion and shrinkage

Concrete has a very low coefficient of thermal expansion. However if no provision is made for expansion very large forces can be created, causing cracks in parts of the structure not capable of withstanding the force or the repeated cycles of expansion and contraction.
As concrete matures it continues to shrink, due to the ongoing reaction taking place in the material, although the rate of shrinkage falls relatively quickly and keeps reducing over time (for all practical purposes concrete is usually considered to not shrink any further after 30 years). The relative shrinkage and expansion of concrete and brickwork require careful accommodation when the two forms of construction interface.
Because concrete is continuously shrinking for years after it is initially placed, it is generally accepted that under thermal loading it will never expand to its originally placed volume.

Cracking

Salginatobel Bridge

One of the early designers of reinforced concrete, Robert Maillart, employed reinforced concrete in a number of arched bridges. His first bridge was simple, using a large volume of concrete. He then realized that much of the concrete was very cracked, and could not be a part of the structure under compressive loads, yet the structure clearly worked.
His later designs simply removed the cracked areas, leaving slender, beautiful concrete arches. The Salginatobel Bridge is an example of this.
Concrete cracks due to tensile stress induced by shrinkage or stresses occurring during setting or use.
Various means are used to overcome this. Fiber reinforced concrete uses fine fibers distributed throughout the mix or larger metal or other reinforcement elements to limit the size and extent of cracks.
In many large structures joints or concealed saw-cuts are placed in the concrete as it sets to make the inevitable cracks occur where they can be managed and out of sight.
Water tanks and highways are examples of structures requiring crack control.

Shrinkage cracking

Shrinkage cracks occur when concrete members undergo restrained volumetric changes (shrinkage) as a result of either drying, autogenous shrinkage or thermal effects. Restraint is provided either externally (i.e. supports, walls, and other boundary conditions) or internally (differential drying shrinkage, reinforcement). Once the tensile strength of the concrete is exceeded, a crack will develop. The number and width of shrinkage cracks that develop are influenced by the amount of shrinkage that occurs, the amount of restraint present and the amount and spacing of reinforcement provided.
Concrete is placed while in a wet (or plastic) state, and therefore can be manipulated and moulded as needed. Hydration and hardening of concrete during the first three days is critical. Abnormally fast drying and shrinkage due to factors such as evaporation from wind during placement may lead to increased tensile stresses at a time when it has not yet gained significant strength, resulting in greater shrinkage cracking. The early strength of the concrete can be increased by keeping it damp for a longer period during the curing process. Minimizing stress prior to curing minimizes cracking. High early-strength concrete is designed to hydrate faster, often by increased use of cement which increases shrinkage and cracking.
Plastic-shrinkage cracks are immediately apparent, visible within 0 to 2 days of placement, while drying-shrinkage cracks develop over time.

Tension cracking

Concrete members may be put into tension by applied loads. This is most common in concrete beams where a transversely applied load will put one surface into compression and the opposite surface into tension due to induced bending. The portion of the beam that is in tension may crack. The size and length of cracks is dependent on the magnitude of the bending moment and the design of the reinforcing in the beam at the point under consideration. Reinforced concrete beams are designed to crack in tension rather than in compression. This is achieved by providing reinforcing steel which yields before failure of the concrete in compression occurs and allowing remediation, repair, or if necessary, evacuation of an unsafe area.

Creep

Creep is the term used to describe the permanent movement or deformation of a material in order to relieve stresses within the material. Concrete which is subjected to forces is prone to creep. Creep can sometimes reduce the amount of cracking that occurs in a concrete structure or element, but it also must be controlled. The amount of primary and secondary reinforcing in concrete structures contributes to a reduction in the amount of shrinkage, creep and cracking.

Because it is a fluid, concrete can be pumped to where it is needed. Here a concrete transport truck is feeding concrete to a concrete pumper, which is pumping it to where a slab is being poured.

Physical properties

The coefficient of thermal expansion of Portland cement concrete is 0.000008 to 0.000012 (per degree Celsius) (8-12 1/MK).
The density varies, but is around 150 pounds per cubic foot (2400 kg/m³).

Damage modes

Fire

Due to its low thermal conductivity, a layer of concrete is frequently used for fireproofing of steel structures. However, concrete itself may be damaged by fire.
Up to about 300 °C, the concrete undergoes normal thermal expansion. Above that temperature, shrinkage occurs due to water loss; however, the aggregate continues expanding, which causes internal stresses. Up to about 500 °C, the major structural changes are carbonation and coarsening of pores. At 573 °C, quartz undergoes rapid expansion due to Phase transition, and at 900 °C calcite starts shrinking due to decomposition. At 450-550 °C the cement hydrate decomposes, yielding calcium oxide. Calcium carbonate decomposes at about 600 °C. Rehydration of the calcium oxide on cooling of the structure causes expansion, which can cause damage to material which withstood fire without falling apart. Concrete in buildings that experienced a fire and were left standing for several years shows extensive degree of carbonation.
Concrete exposed to up to 100 °C is normally considered as healthy. The parts of a concrete structure that is exposed to temperatures above approximately 300 °C (dependent of water/cement ratio) will most likely get a pink color. Over approximately 600 °C the concrete will turn light grey, and over approximately 1000 °C it turns yellow-brown.[16] One rule of thumb is to consider all pink colored concrete as damaged, and to be removed.
Fire will expose the concrete to gasses and liquids that can be harmful to the concrete, among other salts and acids that occur when fire-gasses get in contact with water.

Aggregate expansion

Various types of aggregate undergo chemical reactions in concrete, leading to damaging expansive phenomena. The most common are those containing reactive silica, that can react (in the presence of water) with the alkalis in concrete (K2O and Na2O, coming principally from cement). Among the more reactive mineral components of some aggregates are opal, chalcedony, flint and strained quartz. Following the reaction (Alkali Silica Reaction or ASR), an expansive gel forms, that creates extensive cracks and damage on structural members. On the surface of concrete pavements the ASR can cause pop-outs, i.e. the expulsion of small cones (up to 3 cm about in diameter) in correspondence of aggregate particles. When some aggregates containing dolomite are used, a dedolomitization reaction occurs where the magnesium carbonate compound reacts with hydroxyl ions and yields magnesium hydroxide and a carbonate ion. The resulting expansion may cause destruction of the material. Far less common are pop-outs caused by the presence of pyrite, an iron sulfide that generates expansion by forming iron oxide and ettringite. Other reactions and recrystallizations, e.g. hydration of clay minerals in some aggregates, may lead to destructive expansion as well.

Sea water effects

Concrete exposed to sea water is susceptible to its corrosive effects. The effects are more pronounced above the tidal zone than where the concrete is permanently submerged. In the submerged zone, magnesium and hydrogen carbonate ions precipitate about 30 micrometers thick layer of brucite on which a slower deposition of calcium carbonate as aragonite occurs. These layers somewhat protect the concrete from other processes, which include attack by magnesium, chloride and sulfate ions and carbonation. Above the water surface, mechanical damage may occur by erosion by waves themselves or sand and gravel they carry, and by crystallization of salts from water soaking into the concrete pores and then drying up. Pozzolanic cements and cements using more than 60% of slag as aggregate are more resistant to sea water than pure Portland cement.

Bacterial corrosion

Bacteria themselves do not have noticeable effect on concrete. However, anaerobic bacteria (Thiobacillus) in untreated sewage tend to produce hydrogen sulfide, which is then oxidized by aerobic bacteria present in biofilm on the concrete surface above the water level to sulfuric acid which dissolves the carbonates in the cured cement and causes strength loss. Concrete floors lying on ground containing pyrite are also at risk. Using limestone as the aggregate makes the concrete more resistant to acids, and the sewage may be pretreated by ways increasing pH or oxidizing or precipitating the sulphides in order to inhibit the activity of sulphide utilizing bacteria.

Chemical attacks

Carbonation

Chlorides

Chlorides, particularly calcium chloride, have been used to shorten the setting time of concrete.[17] However, calcium chloride and (to a lesser extent) sodium chloride have been shown to leach calcium hydroxide and cause chemical changes in Portland cement, leading to loss of strength,[18] as well as attacking the steel reinforcement present in most concrete.

Sulphates

Sulphates in solution in contact with concrete can cause chemical changes to the cement, which can cause significant microstructural effects leading to the weakening of the cement binder.

Leaching

Physical damage

Damage can occur during the casting and de-shuttering processes. The corners of beams for instance, can be damaged during the removal of shuttering because they are less effectively compacted by means of vibration (improved by using form-vibrators). Other physical damage can be caused by the use of steel shuttering without base plates. The steel shuttering pinches the top surface of a concrete slab due to weight of the next slab being constructed.

Types of concrete

Various types of concrete have been developed for specialist application and have become known by these names.

Regular concrete

Regular concrete paving blocks
Regular concrete is the lay term describing concrete that is produced by following the mixing instructions that are commonly published on packets of cement, typically using sand or other common material as the aggregate, and often mixed in improvised containers. This concrete can be produced to yield a varying strength from about 10 MPa to about 40 MPa, depending on the purpose, ranging from blinding to structural concrete respectively. Many types of pre-mixed concrete are available which include powdered cement mixed with an aggregate, needing only water.
Typically, a batch of concrete can be made by using 1 part portland cement, 2 parts dry sand, 3 parts dry stone, 1/2 part water. The parts are in terms of weight – not volume. For example, 1 cubic foot of concrete would be made using 22 lbs cement, 10 lbs water, 41 lbs dry sand, 70 lbs dry stone (1/2" to 3/4" stone). This would make 1 cubic foot of concrete and would weigh about 143 lbs. The sand should be mortar or brick sand (washed and filtered if possible) and the stone should be washed if possible. Organic materials (leaves, twigs, etc) should be removed from the sand and stone to ensure the highest strength.

High-strength concrete

High-strength concrete has a compressive strength generally greater than 6,000 pounds per square inch (40 MPA). High-strength concrete is made by lowering the water-cement (W/C) ratio to 0.35 or lower. Often silica fume is added to prevent the formation of free calcium hydroxide crystals in the cement matrix, which might reduce the strength at the cement-aggregate bond.
Low W/C ratios and the use of silica fume make concrete mixes significantly less workable, which is particularly likely to be a problem in high-strength concrete applications where dense rebar cages are likely to be used. To compensate for the reduced workability, superplasticizers are commonly added to high-strength mixtures. Aggregate must be selected carefully for high-strength mixes, as weaker aggregates may not be strong enough to resist the loads imposed on the concrete and cause failure to start in the aggregate rather than in the matrix or at a void, as normally occurs in regular concrete.
In some applications of high-strength concrete the design criterion is the elastic modulus rather than the ultimate compressive strength.

High-performance concrete

High-performance concrete (HPC) is a relatively new term used to describe concrete that conforms to a set of standards above those of the most common applications, but not limited to strength. While all high-strength concrete is also high-performance, not all high-performance concrete is high-strength. Some examples of such standards currently used in relation to HPC are:
Ease of placement
Compaction without segregation
Early age strength
Long-term mechanical properties
Permeability
Density
Heat of hydration
Toughness
Volume stability
Long life in severe environments

Self-compacting concretes

During the 1980s a number of countries including Japan, Sweden and France developed concretes that are self-compacting, known as self-consolidating concrete in the United States. This self-compacting concrete (SCCs) is characterized by:
extreme fluidity as measured by flow, typically between 650-750 mm on a flow table, rather than slump(height)
no need for vibrators to compact the concrete
placement being easier.
no bleed water, or aggregate segregation
SCC can save up to 50% in labor costs due to 80% faster pouring and reduced wear and tear on formwork.
As of 2005, self-compacting concretes account for 10-15% of concrete sales in some European countries. In the US precast concrete industry, SCC represents over 75% of concrete production. 38 departments of transportation in the US accept the use of SCC for road and bridge projects.
This emerging technology is made possible by the use of polycarboxylates plasticizer instead of older naphthalene based polymers, and viscosity modifiers to address aggregate segregation.

Shotcrete

Main article: Shotcrete

Shotcrete (occasionally also known as Gunite) uses compressed air to shoot concrete onto (or into) a frame or structure. Shotcrete is frequently used against vertical soil or rock surfaces, as it eliminates the need for formwork. It is sometimes used for rock support, especially in tunnelling.
There are two application methods for shotcrete.
dry-mix – the dry mixture of cement and aggregates is filled into the machine and conveyed with compressed air through the hoses. The water needed for the hydration is added at the nozzle.
wet-mix – the mixes are prepared with all necessary water for hydration. The mixes are pumped through the hoses. At the nozzle compressed air is added for spraying.
For both methods additives such as accelerators and fiber reinforcement may be used.

Pervious concrete

Pervious concrete contains a network of holes or voids, to allow air or water to move through the concrete.
It is formed by leaving out some or all of the fine aggregate (fines), the remaining large aggregate then is bound by a relatively small amount of cement paste. When set, typically between 15 and 25% of the concrete volume are voids, allowing water to drain at around 5 gal/ft²/ min or 200 L/m²/min) through the concrete.
Pervious concrete allows water to drain naturally through roadway or other structures, reducing the amount of artificial drainage needed, and allowing the water to naturally replenish groundwater
It can significantly reduce noise, by allowing air squeezed between vehicle tyres and the roadway to escape.

Cellular concrete

Aerated concrete produced by the addition of an air entraining agent to the concrete (or a lightweight aggregate like expanded clay pellets or cork granules and vermiculite) is sometimes called Cellular concrete.
See also: Aerated autoclaved concrete

Cork-cement composites

Cork granules are obtained during production of bottle stoppers from the treated bark of Cork oak or Quercus suber trees.These trees are mainly found in Portugal, Spain and North Africa. Portugal is the largest cork producing country, followed by Spain. The waste cork granules have a density of about 300 kg/m³, which is lower than that of most of the lightweight aggregates used for making lightweight concrete. It has been found that cork granules do not significantly influence cement hydration. However, cork dust can influence hydration. Cork cement composites have several advantages over standard concrete, such as lower thermal conductivities, lower densities and good energy absorption characteristics. These composites can be made of density from 400 to 1500 kg/m³, compressive strength from 1 to 26 MPa, and flexural strength from 0.5 to 4.0 MPa.

Roller-compacted concrete

Roller-compacted concrete, sometimes called rollcrete, is a low-cement-content stiff concrete placed using techniques borrowed from earthmoving and paving work. The concrete is placed on the surface to be covered, and is compacted in place using large heavy rollers typically used in earthwork. The concrete mix achieves a high density and cures over time into a strong monolithic block.Roller-compacted concrete is typically used for concrete pavement, but has also been used to build concrete dams, as the low cement content causes less heat to be generated while curing than typical for conventionally placed massive concrete pours.

Glass concrete

The use of recycled glass as aggregate in concrete has become popular in modern times, with large scale research being carried out at Columbia University in New York. This greatly enhances the aesthetic appeal of the concrete. Resent research findings have shown that concrete made with recycled glass aggregates have shown better long term strength and better thermal insulation due to its better thermal properties of the glass aggregates.

Asphalt concrete

Strictly speaking, asphalt is a form of concrete as well, with bituminous materials replacing cement as the binder.

Rapid strength concrete

This type of concrete is able to develop high resistance within few hours after been manufactured. This feature has advantages such as removing the formwork early and to move forward in the building process at record time, repair road surfaces that become fully operational in just few hours.

Rubberized concrete

While "rubberized asphalt concrete" is common, rubberized Portland cement concrete ("rubberized PCC") is still undergoing experimental tests, as of 2007

Polymer concrete

Polymer concrete is concrete which uses polymers to bind the aggregate. Polymer concrete can gain a lot of strength in a short amount of time. For example, a polymer mix may reach 5000 psi in only four hours. Polymer concrete is generally more expensive than conventional concretes.

Limecrete

Limecrete or lime concrete is concrete where cement is replaced by lime.

Concrete testing

Compression testing of a concrete cylinder

Same cylinder after failure

Engineers usually specify the required compressive strength of concrete, which is normally given as the 28 day compressive strength in megapascals (MPa) or pounds per square inch (psi). Twenty eight days is a long wait to determine if desired strengths are going to be obtained, so three-day and seven-day strengths can be useful to predict the ultimate 28-day compressive strength of the concrete. A 25% strength gain between 7 and 28 days is often observed with 100% OPC (ordinary Portland cement) mixtures, and up to 40% strength gain can be realized with the inclusion of pozzolans and supplementary cementitious materials (SCM's) such as fly ash and/or slag cement. As strength gain depends on the type of mixture, its constituents, the use of standard curing, proper testing and care of cylinders in transport, etc. it becomes imperative to proactively rely on testing the fundamental properties of concrete in its fresh, plastic state.
Concrete is typically sampled while being placed, with testing protocols requiring that test samples be cured under laboratory conditions (standard cured). Additional samples may be field cured (non-standard) for the purpose of early 'stripping' strengths, that is, form removal, evaluation of curing, etc. but the standard cured cylinders comprise acceptance criteria. Concrete tests can measure the "plastic" (unhydrated) properties of concrete prior to, and during placement. As these properties affect the hardened compressive strength and durability of concrete (resistance to freeze-thaw) , the properties of slump (workability), temperature, density and age are monitored to ensure the production and placement of 'quality' concrete. Tests are performed per ASTM International or CSA (Canadian Standards Association) and European methods and practices. Technicians performing concrete tests MUST be certified. Structural design, material design and properties are often specified in accordance with ACI American Concrete Institute) code (www.concrete.org); with test methods, production and delivery under the "prescription" or "performance" purchasing options per ASTM C94 (www.astm.org).
Compressive strength tests are conducted using an instrumented hydraulic ram to compress a cylindrical or cubic sample to failure. Tensile strength tests are conducted either by three-point bending of a prismatic beam specimen or by compression along the sides of a cylindrical specimen.

Concrete recycling

Main article: Concrete recycling

Concrete recycling is an increasingly common method of disposing of concrete structures. Concrete debris was once routinely shipped to landfills for disposal, but recycling is increasing due to improved environmental awareness, governmental laws, and economic benefits.
Concrete, which must be free of trash, wood, paper and other such materials is collected from demolition sites and put through a crushing machine, often along with asphalt, bricks, and rocks.
Reinforced concrete contains rebar and other metallic reinforcements, which are removed with magnets and recycled elsewhere. The remaining aggregate chunks are sorted by size. Larger chunks may go through the crusher again. Smaller pieces of concrete are used as gravel for new construction projects. Aggregate base gravel is laid down as the lowest layer in a road, with fresh concrete or asphalt placed over it. Crushed recycled concrete can sometimes be used as the dry aggregate for brand new concrete if it is free of contaminants, though the use of recycled concrete limits strength and is not allowed in many jurisdictions. On March 3, 1983, a government funded research team (the VIRL research.codep) approximated that almost 17% of worldwide landfill was byproducts of concrete based waste.
Recycling concrete provides environmental benefits, conserving landfill space and use as aggregate reduces the need for gravel mining.

Use of concrete in structures

Mass concrete structures

These include gravity dams such as the Hoover Dam and the Three Gorges Dam and large breakwaters. Concrete that is poured all at once in one block (so that there are no weak points where the concrete is "welded" together) is used for tornado shelters.

Reinforced concrete structures

Main article: Reinforced concrete
Reinforced concrete contains steel reinforcing that is designed and placed in structural members at specific positions to cater for all the stress conditions that the member is required to accommodate.

Prestressed concrete structures

Main article: Prestressed concrete

Prestressed concrete is a form of reinforced concrete which builds in compressive stresses during construction to oppose those found when in use. This can greatly reduce the weight of beams or slabs, by better distributing the stresses in the structure to make optimal use of the reinforcement.
For example a horizontal beam will tend to sag down. If the reinforcement along the bottom of the beam is prestressed, it can counteract this.
In pre-tensioned concrete, the prestressing is achieved by using steel or polymer tendons or bars that are subjected to a tensile force prior to casting, or for post-tensioned concrete, after casting.